OXIDIZED BITUMEN 150/5 http://oxidizedbitumen.org/bitumen-1/oxidized-asphalt-150-5/11-content/samples Sun, 08 Jun 2025 00:37:33 +0000 Joomla! - Open Source Content Management fa-ir site@oxidizedbitumen.org (oxidizedbitumen.org) BITUMEN PERFORMANCE GRADE 58/16 http://oxidizedbitumen.org/bitumen-grade/bitumen-performance-grade/bitumen-performance-grade-58-16 http://oxidizedbitumen.org/bitumen-grade/bitumen-performance-grade/bitumen-performance-grade-58-16 BITUMEN PG 58/16  PERFORMANCE GRADE SPECIFICATION UNIT VALUE METHOD Maximum Pavement Design Temp. Degree Celsius (°C) 46 ASTM D6373 Maximum Pavement Design Temp. Degree Celsius (°C) – 34 ASTM D6373 Flash Point (Cleveland Open Cup) Degree Celsius (°C) 230 min ASTM D92 Rotational Viscosity, 135°C Pascal Second (Pa.s) 3 max ASTM D4402 Dynamic Shear, 70°C Degree Celsius (°C) 46 min ASTM D6373 Mass Loss Weight Percentage (WT %) 1 max ASTM D6 Creep Stiffness Degree Celsius (°C) -24 ASTM D6648 Direct Tension Degree Celsius (°C) -24 ASTM D6723 Absolute Viscosity, 60°C Poise (P) 295 ASTM D4402 Penetration, 25°C 1/10 Millimetres (mm) 300 ASTM D5 Specific Gravity Kilogram per Cubic Meter (kg/m³) 1.026 min ASTM D70  APPLICATION TEMPERATURE APPLICATION UNIT RECOMMENDED TEMPERATURE Storage Temperature Degree Celsius (°C) 50-163 Spraying Temperature Degree Celsius (°C) 177 max ]]> adas@wd.com (Super User) Samples Sat, 11 May 2013 23:14:11 +0000 BITUMEN PERFORMANCE GRADE 46/22 http://oxidizedbitumen.org/bitumen-grade/bitumen-performance-grade/bitumen-performance-grade-46-22 http://oxidizedbitumen.org/bitumen-grade/bitumen-performance-grade/bitumen-performance-grade-46-22 BITUMEN PG 46/22  PERFORMANCE GRADE SPECIFICATION UNIT VALUE METHOD Maximum Pavement Design Temp. Degree Celsius (°C) 46 ASTM D6373 Maximum Pavement Design Temp. Degree Celsius (°C) – 34 ASTM D6373 Flash Point (Cleveland Open Cup) Degree Celsius (°C) 230 min ASTM D92 Rotational Viscosity, 135°C Pascal Second (Pa.s) 3 max ASTM D4402 Dynamic Shear, 70°C Degree Celsius (°C) 46 min ASTM D6373 Mass Loss Weight Percentage (WT %) 1 max ASTM D6 Creep Stiffness Degree Celsius (°C) -24 ASTM D6648 Direct Tension Degree Celsius (°C) -24 ASTM D6723 Absolute Viscosity, 60°C Poise (P) 295 ASTM D4402 Penetration, 25°C 1/10 Millimetres (mm) 300 ASTM D5 Specific Gravity Kilogram per Cubic Meter (kg/m³) 1.026 min ASTM D70  APPLICATION TEMPERATURE APPLICATION UNIT RECOMMENDED TEMPERATURE Storage Temperature Degree Celsius (°C) 50-163 Spraying Temperature Degree Celsius (°C) 177 max ]]> adas@wd.com (Super User) Samples Sat, 11 May 2013 23:13:54 +0000 BITUMEN CLASS 600 http://oxidizedbitumen.org/bitumen-grade/australian-grades-bitumen/bitumen-class-600 http://oxidizedbitumen.org/bitumen-grade/australian-grades-bitumen/bitumen-class-600 Class 600 bitumen is primarily used to manufacture extra heavy-duty asphalt pavements that need to endure substantial traffic loadings.

Applications bitumen C600

bitumen C600 is the hardest paving grade bitumen available in Australia and is mainly used to produce high modulus asphalt.
Heavy duty asphalt pavements need to be designed to accommodate significant traffic loadings for up to 40 years without exhibiting structural failure and hence, need to be constructed using appropriate materials.
The load spreading characteristics of pavement layers are governed by their stiffness and C600 bitumen facilitates the production of high modulus asphalt.



Asphalt recommendations
  Mixing Temperature Holding time at Mixing Temperature Medium term storage temperature Medium term storage time Maximum safe handling temperature
175 – 185°C 14 days 130-150°C 30 days 190°C



Typical characteristics
Description Units Methods Typical
Viscosity at 60° Pa.s AS 2341.2 600
Viscosity at 135° Pa.s AS 2341.2 0.7
Pen at 25° dmm AS 2341.12 min 20
Flashpoint °C AS 2341.14 max 250
Viscosity of residue at 60° C (% of original)   Pa.s   AS 2341.2   max 300