Penetration Bitumen Grade 80/100
Bitumen grade 80/100 is a premium brand that is dark brown or black color similar to cement-shape semi-solid or viscous liquid form produced by the non-destructive refining of crude oil during petroleum refining.
The exact chemical composition of bitumen is dependent on the chemical complexity of the original crude oil and the manufacturing process.
Penetration bitumen grade 80/100 has properties of 80~100 desimilimeter and softening point 42~50 Deg.C.
Bitumen 80/100 could also be a specialist fuel grade, typically exclusively created in regarding 65th of refineries around the world and with a yield of exclusively 3%~4% of the total crude slate, bituminous crudes from the likes of oil countries tend to supply rather additional, but these a further specialized refinement methodology, means that on the way facet the potential of most ancient refineires.
Application of bitumen 80/100 grade:Penetration bitumen grade 80/100 is used for paving, road construction and used for hot mixed asphalt because of the properties of very strong viscosity compared to other grade.
Bitumen 80/100 is Elastic and Plastic:
When one takes a thread of bitumen 80/100 from a sample and stretches or elongates it, it is the power to return to a length preparing to its original length eventually.
For many bitumen 80/100 this technique might take longer than others.
When temperatures unit of measurement raised, equally as once a load is applied to bitumen 80/100, the bitumen 80/100 will flow, but will not come back to its original position once load is removed.
This condition is alleged as plastic behavior. Applying a load implies that you simply place a weight on the bitumen 80/100 therefore on subject it to fret.
This may well be throughout a groundwork science lab or at intervals the bitumen 80/100 final position at intervals the road and it's done to assess the bitumen 80/100 reaction to the load.
Data Sheet of penetration bitumen grade 80/100:
|Bitumen 80/100||Specification||Test method|
|Specific Gravity @25/25cg||1.01/1.06||D-70|
|Penetration @25 Deg.C||80/100||D-5|
|Softening point, Ddeg.C||42/50||D-36|
|Ductility @ 25 Deg.C||100min||D-113|
|Loss on heating (WT) %||0.2 max||D-6|
|Drop in penetration after heating %||20 max||D-6, D-5|
|Flash point, Deg.C||250 min||D-92|
|Solubility IS CS2(WT) %||99.5 max||D-4|